AISI W2 Steel vs. N08120 Nickel

AISI W2 steel belongs to the iron alloys classification, while N08120 nickel belongs to the nickel alloys. They have a modest 32% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AISI W2 steel and the bottom bar is N08120 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
79
Tensile Strength: Ultimate (UTS), MPa 580 to 2400
700

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 45
11
Thermal Expansion, µm/m-K 12
14

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
45
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 2.0
7.2
Embodied Energy, MJ/kg 29
100
Embodied Water, L/kg 48
240

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 86
24
Strength to Weight: Bending, points 20 to 51
21
Thermal Diffusivity, mm2/s 12
3.0
Thermal Shock Resistance, points 19 to 80
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Boron (B), % 0
0 to 0.010
Carbon (C), % 0.85 to 1.5
0.020 to 0.1
Chromium (Cr), % 0 to 0.15
23 to 27
Cobalt (Co), % 0
0 to 3.0
Copper (Cu), % 0 to 0.2
0 to 0.5
Iron (Fe), % 96.2 to 98.6
21 to 41.4
Manganese (Mn), % 0.35 to 0.74
0 to 1.5
Molybdenum (Mo), % 0 to 0.1
0 to 2.5
Nickel (Ni), % 0 to 0.2
35 to 39
Niobium (Nb), % 0
0.4 to 0.9
Nitrogen (N), % 0
0.15 to 0.3
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.1 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Titanium (Ti), % 0
0 to 0.2
Tungsten (W), % 0 to 0.15
0 to 2.5
Vanadium (V), % 0.15 to 0.35
0