AM60A magnesium belongs to the magnesium alloys classification, while AWS BAg-23 belongs to the otherwise unclassified metals. There are 15 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60A magnesium and the bottom bar is AWS BAg-23.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
90
Poisson's Ratio 0.29
0.36
Shear Modulus, GPa 18
33
Tensile Strength: Ultimate (UTS), MPa 230
170

Thermal Properties

Latent Heat of Fusion, J/g 350
130
Melting Completion (Liquidus), °C 620
970
Melting Onset (Solidus), °C 550
960
Specific Heat Capacity, J/kg-K 1000
270
Thermal Expansion, µm/m-K 26
20

Otherwise Unclassified Properties

Density, g/cm3 1.7
10

Common Calculations

Stiffness to Weight: Axial, points 15
5.0
Stiffness to Weight: Bending, points 71
15
Strength to Weight: Axial, points 37
4.7
Strength to Weight: Bending, points 49
6.8
Thermal Shock Resistance, points 14
6.8

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 5.5 to 6.5
0
Copper (Cu), % 0 to 0.35
0
Magnesium (Mg), % 91.8 to 94.4
0
Manganese (Mn), % 0.13 to 0.6
13.9 to 16
Nickel (Ni), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Silver (Ag), % 0
84 to 86
Zinc (Zn), % 0 to 0.22
0
Residuals, % 0
0 to 0.15