AM60A Magnesium vs. EN 1.1219 Steel

AM60A magnesium belongs to the magnesium alloys classification, while EN 1.1219 steel belongs to the iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60A magnesium and the bottom bar is EN 1.1219 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 62
200 to 220
Elastic (Young's, Tensile) Modulus, GPa 45
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
72
Tensile Strength: Ultimate (UTS), MPa 230
700 to 770

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 120
400
Melting Completion (Liquidus), °C 620
1460
Melting Onset (Solidus), °C 550
1410
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 62
51
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 69
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 12
1.9
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 23
1.4
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 990
47

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 71
24
Strength to Weight: Axial, points 37
25 to 27
Strength to Weight: Bending, points 49
22 to 24
Thermal Diffusivity, mm2/s 37
14
Thermal Shock Resistance, points 14
22 to 25

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0 to 0.050
Carbon (C), % 0
0.52 to 0.6
Copper (Cu), % 0 to 0.35
0 to 0.3
Iron (Fe), % 0
98.3 to 99.4
Magnesium (Mg), % 91.8 to 94.4
0
Manganese (Mn), % 0.13 to 0.6
0.6 to 0.9
Nickel (Ni), % 0 to 0.030
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.5
0 to 0.4
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.22
0