AM60A Magnesium vs. EN 1.4805 Stainless Steel

AM60A magnesium belongs to the magnesium alloys classification, while EN 1.4805 stainless steel belongs to the iron alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60A magnesium and the bottom bar is EN 1.4805 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 62
140
Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 8.8
9.0
Fatigue Strength, MPa 70
130
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 18
77
Tensile Strength: Ultimate (UTS), MPa 230
490
Tensile Strength: Yield (Proof), MPa 130
250

Thermal Properties

Latent Heat of Fusion, J/g 350
310
Maximum Temperature: Mechanical, °C 120
1000
Melting Completion (Liquidus), °C 620
1390
Melting Onset (Solidus), °C 550
1350
Specific Heat Capacity, J/kg-K 1000
480
Thermal Conductivity, W/m-K 62
14
Thermal Expansion, µm/m-K 26
16

Otherwise Unclassified Properties

Base Metal Price, % relative 12
26
Density, g/cm3 1.7
7.9
Embodied Carbon, kg CO2/kg material 23
4.7
Embodied Energy, MJ/kg 160
66
Embodied Water, L/kg 990
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 17
37
Resilience: Unit (Modulus of Resilience), kJ/m3 190
150
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 71
25
Strength to Weight: Axial, points 37
17
Strength to Weight: Bending, points 49
18
Thermal Diffusivity, mm2/s 37
3.7
Thermal Shock Resistance, points 14
11

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0
0.2 to 0.5
Chromium (Cr), % 0
19 to 23
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 0
44.9 to 56.8
Magnesium (Mg), % 91.8 to 94.4
0
Manganese (Mn), % 0.13 to 0.6
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0 to 0.030
23 to 27
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.5
1.0 to 2.0
Sulfur (S), % 0
0 to 0.030
Zinc (Zn), % 0 to 0.22
0