AM60A Magnesium vs. CC140C Copper

AM60A magnesium belongs to the magnesium alloys classification, while CC140C copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60A magnesium and the bottom bar is CC140C copper.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 62
110
Elastic (Young's, Tensile) Modulus, GPa 45
120
Elongation at Break, % 8.8
11
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 18
44
Tensile Strength: Ultimate (UTS), MPa 230
340
Tensile Strength: Yield (Proof), MPa 130
230

Thermal Properties

Latent Heat of Fusion, J/g 350
210
Maximum Temperature: Mechanical, °C 120
200
Melting Completion (Liquidus), °C 620
1100
Melting Onset (Solidus), °C 550
1040
Specific Heat Capacity, J/kg-K 1000
390
Thermal Conductivity, W/m-K 62
310
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
77
Electrical Conductivity: Equal Weight (Specific), % IACS 69
78

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 1.7
8.9
Embodied Carbon, kg CO2/kg material 23
2.6
Embodied Energy, MJ/kg 160
41
Embodied Water, L/kg 990
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 17
34
Resilience: Unit (Modulus of Resilience), kJ/m3 190
220
Stiffness to Weight: Axial, points 15
7.3
Stiffness to Weight: Bending, points 71
18
Strength to Weight: Axial, points 37
10
Strength to Weight: Bending, points 49
12
Thermal Diffusivity, mm2/s 37
89
Thermal Shock Resistance, points 14
12

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0
Chromium (Cr), % 0
0.4 to 1.2
Copper (Cu), % 0 to 0.35
98.8 to 99.6
Magnesium (Mg), % 91.8 to 94.4
0
Manganese (Mn), % 0.13 to 0.6
0
Nickel (Ni), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Zinc (Zn), % 0 to 0.22
0