AM60A Magnesium vs. SAE-AISI 8622 Steel

AM60A magnesium belongs to the magnesium alloys classification, while SAE-AISI 8622 steel belongs to the iron alloys. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60A magnesium and the bottom bar is SAE-AISI 8622 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 62
150
Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 8.8
26
Fatigue Strength, MPa 70
240
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
73
Shear Strength, MPa 130
320
Tensile Strength: Ultimate (UTS), MPa 230
500
Tensile Strength: Yield (Proof), MPa 130
330

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 120
410
Melting Completion (Liquidus), °C 620
1460
Melting Onset (Solidus), °C 550
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 62
38
Thermal Expansion, µm/m-K 26
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 69
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.6
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 23
1.5
Embodied Energy, MJ/kg 160
20
Embodied Water, L/kg 990
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 17
110
Resilience: Unit (Modulus of Resilience), kJ/m3 190
280
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 71
24
Strength to Weight: Axial, points 37
18
Strength to Weight: Bending, points 49
18
Thermal Diffusivity, mm2/s 37
10
Thermal Shock Resistance, points 14
17

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0
0.2 to 0.25
Chromium (Cr), % 0
0.4 to 0.6
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 0
96.9 to 98
Magnesium (Mg), % 91.8 to 94.4
0
Manganese (Mn), % 0.13 to 0.6
0.7 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 0 to 0.030
0.4 to 0.7
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 0 to 0.22
0