AM60A Magnesium vs. C16200 Copper

AM60A magnesium belongs to the magnesium alloys classification, while C16200 copper belongs to the copper alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60A magnesium and the bottom bar is C16200 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
120
Elongation at Break, % 8.8
2.0 to 56
Fatigue Strength, MPa 70
100 to 210
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 18
43
Shear Strength, MPa 130
190 to 390
Tensile Strength: Ultimate (UTS), MPa 230
240 to 550
Tensile Strength: Yield (Proof), MPa 130
48 to 470

Thermal Properties

Latent Heat of Fusion, J/g 350
210
Maximum Temperature: Mechanical, °C 120
370
Melting Completion (Liquidus), °C 620
1080
Melting Onset (Solidus), °C 550
1030
Specific Heat Capacity, J/kg-K 1000
380
Thermal Conductivity, W/m-K 62
360
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
90
Electrical Conductivity: Equal Weight (Specific), % IACS 69
90

Otherwise Unclassified Properties

Base Metal Price, % relative 12
30
Density, g/cm3 1.7
9.0
Embodied Carbon, kg CO2/kg material 23
2.6
Embodied Energy, MJ/kg 160
41
Embodied Water, L/kg 990
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 17
10 to 99
Resilience: Unit (Modulus of Resilience), kJ/m3 190
10 to 970
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 71
18
Strength to Weight: Axial, points 37
7.4 to 17
Strength to Weight: Bending, points 49
9.6 to 17
Thermal Diffusivity, mm2/s 37
100
Thermal Shock Resistance, points 14
8.7 to 20

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0
Cadmium (Cd), % 0
0.7 to 1.2
Copper (Cu), % 0 to 0.35
98.6 to 99.3
Iron (Fe), % 0
0 to 0.2
Magnesium (Mg), % 91.8 to 94.4
0
Manganese (Mn), % 0.13 to 0.6
0
Nickel (Ni), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Zinc (Zn), % 0 to 0.22
0