AM60A Magnesium vs. C18100 Copper

AM60A magnesium belongs to the magnesium alloys classification, while C18100 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60A magnesium and the bottom bar is C18100 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
120
Elongation at Break, % 8.8
8.3
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 18
47
Shear Strength, MPa 130
300
Tensile Strength: Ultimate (UTS), MPa 230
510
Tensile Strength: Yield (Proof), MPa 130
460

Thermal Properties

Latent Heat of Fusion, J/g 350
210
Maximum Temperature: Mechanical, °C 120
200
Melting Completion (Liquidus), °C 620
1080
Melting Onset (Solidus), °C 550
1020
Specific Heat Capacity, J/kg-K 1000
390
Thermal Conductivity, W/m-K 62
320
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
80
Electrical Conductivity: Equal Weight (Specific), % IACS 69
81

Otherwise Unclassified Properties

Base Metal Price, % relative 12
31
Density, g/cm3 1.7
8.9
Embodied Carbon, kg CO2/kg material 23
2.7
Embodied Energy, MJ/kg 160
43
Embodied Water, L/kg 990
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 17
40
Resilience: Unit (Modulus of Resilience), kJ/m3 190
900
Stiffness to Weight: Axial, points 15
7.3
Stiffness to Weight: Bending, points 71
18
Strength to Weight: Axial, points 37
16
Strength to Weight: Bending, points 49
16
Thermal Diffusivity, mm2/s 37
94
Thermal Shock Resistance, points 14
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 5.5 to 6.5
0
Chromium (Cr), % 0
0.4 to 1.2
Copper (Cu), % 0 to 0.35
98.7 to 99.49
Magnesium (Mg), % 91.8 to 94.4
0.030 to 0.060
Manganese (Mn), % 0.13 to 0.6
0
Nickel (Ni), % 0 to 0.030
0
Silicon (Si), % 0 to 0.5
0
Zinc (Zn), % 0 to 0.22
0
Zirconium (Zr), % 0
0.080 to 0.2
Residuals, % 0
0 to 0.5