AM60B Magnesium vs. AISI 440C Stainless Steel

AM60B magnesium belongs to the magnesium alloys classification, while AISI 440C stainless steel belongs to the iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60B magnesium and the bottom bar is AISI 440C stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
200
Elongation at Break, % 11
2.0 to 14
Fatigue Strength, MPa 96
260 to 840
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
76
Shear Strength, MPa 140
430 to 1120
Tensile Strength: Ultimate (UTS), MPa 230
710 to 1970
Tensile Strength: Yield (Proof), MPa 130
450 to 1900

Thermal Properties

Latent Heat of Fusion, J/g 350
280
Maximum Temperature: Mechanical, °C 120
870
Melting Completion (Liquidus), °C 620
1480
Melting Onset (Solidus), °C 540
1370
Specific Heat Capacity, J/kg-K 1000
480
Thermal Conductivity, W/m-K 61
22
Thermal Expansion, µm/m-K 26
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 72
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 12
9.0
Density, g/cm3 1.7
7.7
Embodied Carbon, kg CO2/kg material 23
2.2
Embodied Energy, MJ/kg 160
31
Embodied Water, L/kg 990
120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21
39 to 88
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 71
25
Strength to Weight: Axial, points 38
26 to 71
Strength to Weight: Bending, points 50
23 to 46
Thermal Diffusivity, mm2/s 37
6.0
Thermal Shock Resistance, points 14
26 to 71

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0
1.0 to 1.2
Chromium (Cr), % 0
16 to 18
Copper (Cu), % 0 to 0.010
0
Iron (Fe), % 0 to 0.0050
78 to 83.1
Magnesium (Mg), % 92.6 to 94.3
0
Manganese (Mn), % 0.24 to 0.6
0 to 1.0
Molybdenum (Mo), % 0
0 to 0.75
Nickel (Ni), % 0 to 0.0020
0
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.015
Zinc (Zn), % 0 to 0.22
0