AM60B Magnesium vs. EN 1.0451 Steel

AM60B magnesium belongs to the magnesium alloys classification, while EN 1.0451 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60B magnesium and the bottom bar is EN 1.0451 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 62
120
Elastic (Young's, Tensile) Modulus, GPa 45
190
Elongation at Break, % 11
27
Fatigue Strength, MPa 96
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 17
73
Shear Strength, MPa 140
270
Tensile Strength: Ultimate (UTS), MPa 230
420
Tensile Strength: Yield (Proof), MPa 130
240

Thermal Properties

Latent Heat of Fusion, J/g 350
250
Maximum Temperature: Mechanical, °C 120
400
Melting Completion (Liquidus), °C 620
1460
Melting Onset (Solidus), °C 540
1420
Specific Heat Capacity, J/kg-K 1000
470
Thermal Conductivity, W/m-K 61
49
Thermal Expansion, µm/m-K 26
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 72
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 1.7
7.9
Embodied Carbon, kg CO2/kg material 23
1.5
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 990
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21
98
Resilience: Unit (Modulus of Resilience), kJ/m3 190
150
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 71
24
Strength to Weight: Axial, points 38
15
Strength to Weight: Bending, points 50
16
Thermal Diffusivity, mm2/s 37
13
Thermal Shock Resistance, points 14
13

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0.020 to 0.060
Carbon (C), % 0
0 to 0.15
Chromium (Cr), % 0
0 to 0.3
Copper (Cu), % 0 to 0.010
0 to 0.3
Iron (Fe), % 0 to 0.0050
97.2 to 99.58
Magnesium (Mg), % 92.6 to 94.3
0
Manganese (Mn), % 0.24 to 0.6
0.4 to 1.2
Molybdenum (Mo), % 0
0 to 0.080
Nickel (Ni), % 0 to 0.0020
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Phosphorus (P), % 0
0 to 0.025
Silicon (Si), % 0 to 0.1
0 to 0.35
Sulfur (S), % 0
0 to 0.010
Titanium (Ti), % 0
0 to 0.040
Vanadium (V), % 0
0 to 0.020
Zinc (Zn), % 0 to 0.22
0