AM60B Magnesium vs. C11400 Copper

AM60B magnesium belongs to the magnesium alloys classification, while C11400 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60B magnesium and the bottom bar is C11400 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
120
Elongation at Break, % 11
2.8 to 51
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 17
43
Shear Strength, MPa 140
150 to 210
Tensile Strength: Ultimate (UTS), MPa 230
220 to 400
Tensile Strength: Yield (Proof), MPa 130
75 to 400

Thermal Properties

Latent Heat of Fusion, J/g 350
210
Maximum Temperature: Mechanical, °C 120
200
Melting Completion (Liquidus), °C 620
1080
Melting Onset (Solidus), °C 540
1030
Specific Heat Capacity, J/kg-K 1000
390
Thermal Conductivity, W/m-K 61
390
Thermal Expansion, µm/m-K 26
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
100
Electrical Conductivity: Equal Weight (Specific), % IACS 72
100

Otherwise Unclassified Properties

Base Metal Price, % relative 12
32
Density, g/cm3 1.7
9.0
Embodied Carbon, kg CO2/kg material 23
2.6
Embodied Energy, MJ/kg 160
42
Embodied Water, L/kg 990
350

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21
11 to 90
Resilience: Unit (Modulus of Resilience), kJ/m3 190
24 to 680
Stiffness to Weight: Axial, points 15
7.2
Stiffness to Weight: Bending, points 71
18
Strength to Weight: Axial, points 38
6.8 to 12
Strength to Weight: Bending, points 50
9.1 to 14
Thermal Diffusivity, mm2/s 37
110
Thermal Shock Resistance, points 14
7.8 to 14

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 5.5 to 6.5
0
Copper (Cu), % 0 to 0.010
99.84 to 99.966
Iron (Fe), % 0 to 0.0050
0
Magnesium (Mg), % 92.6 to 94.3
0
Manganese (Mn), % 0.24 to 0.6
0
Nickel (Ni), % 0 to 0.0020
0
Silicon (Si), % 0 to 0.1
0
Silver (Ag), % 0
0.034 to 0.060
Zinc (Zn), % 0 to 0.22
0
Residuals, % 0
0 to 0.1