AM60B Magnesium vs. N06002 Nickel

AM60B magnesium belongs to the magnesium alloys classification, while N06002 nickel belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AM60B magnesium and the bottom bar is N06002 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 45
210
Elongation at Break, % 11
41
Fatigue Strength, MPa 96
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 17
81
Shear Strength, MPa 140
520
Tensile Strength: Ultimate (UTS), MPa 230
760
Tensile Strength: Yield (Proof), MPa 130
310

Thermal Properties

Latent Heat of Fusion, J/g 350
320
Maximum Temperature: Mechanical, °C 120
990
Melting Completion (Liquidus), °C 620
1360
Melting Onset (Solidus), °C 540
1260
Specific Heat Capacity, J/kg-K 1000
450
Thermal Conductivity, W/m-K 61
9.9
Thermal Expansion, µm/m-K 26
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 13
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 72
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 12
55
Density, g/cm3 1.7
8.5
Embodied Carbon, kg CO2/kg material 23
9.3
Embodied Energy, MJ/kg 160
130
Embodied Water, L/kg 990
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 21
250
Resilience: Unit (Modulus of Resilience), kJ/m3 190
230
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 71
23
Strength to Weight: Axial, points 38
25
Strength to Weight: Bending, points 50
22
Thermal Diffusivity, mm2/s 37
2.6
Thermal Shock Resistance, points 14
19

Alloy Composition

Aluminum (Al), % 5.5 to 6.5
0
Carbon (C), % 0
0.050 to 0.15
Chromium (Cr), % 0
20.5 to 23
Cobalt (Co), % 0
0.5 to 2.5
Copper (Cu), % 0 to 0.010
0
Iron (Fe), % 0 to 0.0050
17 to 20
Magnesium (Mg), % 92.6 to 94.3
0
Manganese (Mn), % 0.24 to 0.6
0 to 1.0
Molybdenum (Mo), % 0
8.0 to 10
Nickel (Ni), % 0 to 0.0020
42.3 to 54
Phosphorus (P), % 0
0 to 0.040
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0
0 to 0.030
Tungsten (W), % 0
0.2 to 1.0
Zinc (Zn), % 0 to 0.22
0