ASTM A148 Cast Steel vs. SAE-AISI 1010 Steel

Both ASTM A148 cast steel and SAE-AISI 1010 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A148 cast steel and the bottom bar is SAE-AISI 1010 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 390
100 to 110
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 5.7 to 25
22 to 31
Fatigue Strength, MPa 280 to 670
150 to 230
Poisson's Ratio 0.29
0.29
Reduction in Area, % 13 to 45
46 to 56
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 630 to 1300
350 to 400
Tensile Strength: Yield (Proof), MPa 390 to 1160
190 to 330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400 to 430
400
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 37 to 47
47
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3 to 7.5
12
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3 to 8.6
14

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3 to 3.3
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5 to 1.7
1.4
Embodied Energy, MJ/kg 20 to 22
18
Embodied Water, L/kg 48 to 53
45

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 71 to 150
82 to 93
Resilience: Unit (Modulus of Resilience), kJ/m3 400 to 3570
100 to 290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22 to 46
12 to 14
Strength to Weight: Bending, points 21 to 34
14 to 15
Thermal Diffusivity, mm2/s 9.9 to 13
13
Thermal Shock Resistance, points 18 to 38
11 to 13

Comparable Variants