ASTM A182 Grade F10 vs. SAE-AISI 5160 Steel
Both ASTM A182 grade F10 and SAE-AISI 5160 steel are iron alloys. They have 71% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is ASTM A182 grade F10 and the bottom bar is SAE-AISI 5160 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 | |
| 200 to 340 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 34 | |
| 12 to 18 |
| Fatigue Strength, MPa | 180 | |
| 180 to 650 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 74 | |
| 73 |
| Shear Strength, MPa | 420 | |
| 390 to 700 |
| Tensile Strength: Ultimate (UTS), MPa | 630 | |
| 660 to 1150 |
| Tensile Strength: Yield (Proof), MPa | 230 | |
| 280 to 1010 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 600 | |
| 420 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1450 |
| Melting Onset (Solidus), °C | 1370 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 15 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 17 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 18 | |
| 2.1 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 51 | |
| 19 |
| Embodied Water, L/kg | 120 | |
| 50 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 73 to 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 140 | |
| 200 to 2700 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 | |
| 23 to 41 |
| Strength to Weight: Bending, points | 21 | |
| 22 to 31 |
| Thermal Shock Resistance, points | 18 | |
| 19 to 34 |
Alloy Composition
| Carbon (C), % | 0.1 to 0.2 | |
| 0.56 to 0.61 |
| Chromium (Cr), % | 7.0 to 9.0 | |
| 0.7 to 0.9 |
| Iron (Fe), % | 66.5 to 72.4 | |
| 97.1 to 97.8 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.75 to 1.0 |
| Nickel (Ni), % | 19 to 22 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.035 |
| Silicon (Si), % | 1.0 to 1.4 | |
| 0.15 to 0.35 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.040 |