ASTM A182 Grade F12 Class 2 vs. ACI-ASTM CD6MN Steel

Both ASTM A182 grade F12 class 2 and ACI-ASTM CD6MN steel are iron alloys. They have 69% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is ACI-ASTM CD6MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
28
Fatigue Strength, MPa 220
370
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 540
730
Tensile Strength: Yield (Proof), MPa 310
510

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 430
1100
Melting Completion (Liquidus), °C 1460
1440
Melting Onset (Solidus), °C 1420
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 43
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
3.4
Embodied Energy, MJ/kg 21
48
Embodied Water, L/kg 52
170

Common Calculations

PREN (Pitting Resistance) 2.8
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
180
Resilience: Unit (Modulus of Resilience), kJ/m3 260
650
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 12
4.4
Thermal Shock Resistance, points 16
20

Alloy Composition

Carbon (C), % 0.1 to 0.2
0 to 0.060
Chromium (Cr), % 0.8 to 1.3
24 to 27
Iron (Fe), % 96.4 to 98.3
62.1 to 70.1
Manganese (Mn), % 0.3 to 0.8
0 to 1.0
Molybdenum (Mo), % 0.44 to 0.65
1.8 to 2.5
Nickel (Ni), % 0
4.0 to 6.0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0.1 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.040