MakeItFrom.com
Menu (ESC)

ASTM A182 Grade F12 Class 2 vs. EN 1.3536 Steel

Both ASTM A182 grade F12 class 2 and EN 1.3536 steel are iron alloys. Their average alloy composition is basically identical. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is EN 1.3536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 540
660

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
440
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.6
Embodied Energy, MJ/kg 21
21
Embodied Water, L/kg 52
55

Common Calculations

PREN (Pitting Resistance) 2.8
2.8
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
23
Strength to Weight: Bending, points 19
22
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 16
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0.1 to 0.2
0.93 to 1.1
Chromium (Cr), % 0.8 to 1.3
1.7 to 2.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.4 to 98.3
96 to 97.4
Manganese (Mn), % 0.3 to 0.8
0.6 to 0.8
Molybdenum (Mo), % 0.44 to 0.65
0.2 to 0.35
Oxygen (O), % 0
0 to 0.0015
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0.1 to 0.6
0.15 to 0.45
Sulfur (S), % 0 to 0.040
0 to 0.030