ASTM A182 Grade F12 Class 2 vs. EN 1.4371 Stainless Steel

Both ASTM A182 grade F12 class 2 and EN 1.4371 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is EN 1.4371 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
220 to 230
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
45 to 51
Fatigue Strength, MPa 220
290 to 340
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 340
520 to 540
Tensile Strength: Ultimate (UTS), MPa 540
740 to 750
Tensile Strength: Yield (Proof), MPa 310
320 to 340

Thermal Properties

Latent Heat of Fusion, J/g 250
280
Maximum Temperature: Mechanical, °C 430
880
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 43
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.6
2.6
Embodied Energy, MJ/kg 21
38
Embodied Water, L/kg 52
140

Common Calculations

PREN (Pitting Resistance) 2.8
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
270 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 260
250 to 300
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
27
Strength to Weight: Bending, points 19
24
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 16
16

Alloy Composition

Carbon (C), % 0.1 to 0.2
0 to 0.030
Chromium (Cr), % 0.8 to 1.3
16 to 17.5
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 96.4 to 98.3
66.7 to 74.4
Manganese (Mn), % 0.3 to 0.8
6.0 to 8.0
Molybdenum (Mo), % 0.44 to 0.65
0
Nickel (Ni), % 0
3.5 to 5.5
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0.1 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.040
0 to 0.015