ASTM A182 Grade F12 Class 2 vs. EN 1.4570 Stainless Steel

Both ASTM A182 grade F12 class 2 and EN 1.4570 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is EN 1.4570 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 22
40
Fatigue Strength, MPa 220
180
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 340
410
Tensile Strength: Ultimate (UTS), MPa 540
610
Tensile Strength: Yield (Proof), MPa 310
210

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 430
930
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 43
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
15
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
3.1
Embodied Energy, MJ/kg 21
43
Embodied Water, L/kg 52
150

Common Calculations

PREN (Pitting Resistance) 2.8
20
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
190
Resilience: Unit (Modulus of Resilience), kJ/m3 260
110
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
22
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 12
4.0
Thermal Shock Resistance, points 16
14

Alloy Composition

Carbon (C), % 0.1 to 0.2
0 to 0.080
Chromium (Cr), % 0.8 to 1.3
17 to 19
Copper (Cu), % 0
1.4 to 1.8
Iron (Fe), % 96.4 to 98.3
65 to 73.5
Manganese (Mn), % 0.3 to 0.8
0 to 2.0
Molybdenum (Mo), % 0.44 to 0.65
0 to 0.6
Nickel (Ni), % 0
8.0 to 10
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0.1 to 0.6
0 to 1.0
Sulfur (S), % 0 to 0.040
0.15 to 0.35