ASTM A182 Grade F12 Class 2 vs. EN 1.6511 Steel

Both ASTM A182 grade F12 class 2 and EN 1.6511 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is EN 1.6511 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
300
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
12
Fatigue Strength, MPa 220
480
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 340
600
Tensile Strength: Ultimate (UTS), MPa 540
990
Tensile Strength: Yield (Proof), MPa 310
770

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 430
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
36
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
3.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.6
Embodied Energy, MJ/kg 21
21
Embodied Water, L/kg 52
53

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 260
1590
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
35
Strength to Weight: Bending, points 19
28
Thermal Diffusivity, mm2/s 12
9.9
Thermal Shock Resistance, points 16
29

Alloy Composition

Carbon (C), % 0.1 to 0.2
0.32 to 0.4
Chromium (Cr), % 0.8 to 1.3
0.9 to 1.2
Iron (Fe), % 96.4 to 98.3
95.6 to 97.2
Manganese (Mn), % 0.3 to 0.8
0.5 to 0.8
Molybdenum (Mo), % 0.44 to 0.65
0.15 to 0.3
Nickel (Ni), % 0
0.9 to 1.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0.1 to 0.6
0 to 0.4
Sulfur (S), % 0 to 0.040
0 to 0.035