ASTM A182 Grade F12 Class 2 vs. EN 1.7336 Steel

Both ASTM A182 grade F12 class 2 and EN 1.7336 steel are iron alloys. Their average alloy composition is basically identical. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is EN 1.7336 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
22
Fatigue Strength, MPa 220
240 to 310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 340
370
Tensile Strength: Ultimate (UTS), MPa 540
590
Tensile Strength: Yield (Proof), MPa 310
340 to 440

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 430
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 43
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
3.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.6
Embodied Energy, MJ/kg 21
21
Embodied Water, L/kg 52
53

Common Calculations

PREN (Pitting Resistance) 2.8
3.2
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
110 to 120
Resilience: Unit (Modulus of Resilience), kJ/m3 260
310 to 510
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
21
Strength to Weight: Bending, points 19
20
Thermal Diffusivity, mm2/s 12
11
Thermal Shock Resistance, points 16
17

Alloy Composition

Carbon (C), % 0.1 to 0.2
0 to 0.17
Chromium (Cr), % 0.8 to 1.3
1.0 to 1.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.4 to 98.3
95.6 to 97.7
Manganese (Mn), % 0.3 to 0.8
0.4 to 0.65
Molybdenum (Mo), % 0.44 to 0.65
0.45 to 0.65
Nickel (Ni), % 0
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0.1 to 0.6
0.5 to 0.8
Sulfur (S), % 0 to 0.040
0 to 0.0050