ASTM A182 Grade F12 Class 2 vs. CC751S Brass

ASTM A182 grade F12 class 2 belongs to the iron alloys classification, while CC751S brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is CC751S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
130
Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 22
5.6
Poisson's Ratio 0.29
0.31
Shear Modulus, GPa 73
40
Tensile Strength: Ultimate (UTS), MPa 540
450
Tensile Strength: Yield (Proof), MPa 310
320

Thermal Properties

Latent Heat of Fusion, J/g 250
190
Maximum Temperature: Mechanical, °C 430
130
Melting Completion (Liquidus), °C 1460
850
Melting Onset (Solidus), °C 1420
810
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 43
110
Thermal Expansion, µm/m-K 13
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
25
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
28

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
24
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 1.6
2.8
Embodied Energy, MJ/kg 21
46
Embodied Water, L/kg 52
330

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
23
Resilience: Unit (Modulus of Resilience), kJ/m3 260
480
Stiffness to Weight: Axial, points 13
7.2
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 19
15
Strength to Weight: Bending, points 19
16
Thermal Diffusivity, mm2/s 12
35
Thermal Shock Resistance, points 16
15

Alloy Composition

Aluminum (Al), % 0
0 to 0.1
Antimony (Sb), % 0
0 to 0.5
Carbon (C), % 0.1 to 0.2
0
Chromium (Cr), % 0.8 to 1.3
0
Copper (Cu), % 0
62.7 to 66
Iron (Fe), % 96.4 to 98.3
0.25 to 0.5
Lead (Pb), % 0
0.8 to 2.2
Manganese (Mn), % 0.3 to 0.8
0 to 0.15
Molybdenum (Mo), % 0.44 to 0.65
0
Nickel (Ni), % 0
0 to 0.8
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0.1 to 0.6
0.65 to 1.1
Sulfur (S), % 0 to 0.040
0
Tin (Sn), % 0
0 to 0.8
Zinc (Zn), % 0
27.9 to 35.6