ASTM A182 Grade F12 Class 2 vs. C17465 Copper

ASTM A182 grade F12 class 2 belongs to the iron alloys classification, while C17465 copper belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is C17465 copper.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
120
Elongation at Break, % 22
5.3 to 36
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
44
Shear Strength, MPa 340
210 to 540
Tensile Strength: Ultimate (UTS), MPa 540
310 to 930
Tensile Strength: Yield (Proof), MPa 310
120 to 830

Thermal Properties

Latent Heat of Fusion, J/g 250
210
Maximum Temperature: Mechanical, °C 430
210
Melting Completion (Liquidus), °C 1460
1080
Melting Onset (Solidus), °C 1420
1030
Specific Heat Capacity, J/kg-K 470
390
Thermal Conductivity, W/m-K 43
220
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
22 to 51
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
23 to 52

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
45
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.6
4.1
Embodied Energy, MJ/kg 21
64
Embodied Water, L/kg 52
310

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
47 to 90
Resilience: Unit (Modulus of Resilience), kJ/m3 260
64 to 2920
Stiffness to Weight: Axial, points 13
7.3
Stiffness to Weight: Bending, points 24
18
Strength to Weight: Axial, points 19
9.7 to 29
Strength to Weight: Bending, points 19
11 to 24
Thermal Diffusivity, mm2/s 12
64
Thermal Shock Resistance, points 16
11 to 33

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.2
Beryllium (Be), % 0
0.15 to 0.5
Carbon (C), % 0.1 to 0.2
0
Chromium (Cr), % 0.8 to 1.3
0
Copper (Cu), % 0
95.7 to 98.7
Iron (Fe), % 96.4 to 98.3
0 to 0.2
Lead (Pb), % 0
0.2 to 0.6
Manganese (Mn), % 0.3 to 0.8
0
Molybdenum (Mo), % 0.44 to 0.65
0
Nickel (Ni), % 0
1.0 to 1.4
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0.1 to 0.6
0 to 0.2
Sulfur (S), % 0 to 0.040
0
Tin (Sn), % 0
0 to 0.25
Zirconium (Zr), % 0
0 to 0.5
Residuals, % 0
0 to 0.5