ASTM A182 Grade F12 Class 2 vs. S30615 Stainless Steel

Both ASTM A182 grade F12 class 2 and S30615 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 63% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F12 class 2 and the bottom bar is S30615 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 22
39
Fatigue Strength, MPa 220
270
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
75
Shear Strength, MPa 340
470
Tensile Strength: Ultimate (UTS), MPa 540
690
Tensile Strength: Yield (Proof), MPa 310
310

Thermal Properties

Latent Heat of Fusion, J/g 250
340
Maximum Temperature: Mechanical, °C 430
960
Melting Completion (Liquidus), °C 1460
1370
Melting Onset (Solidus), °C 1420
1320
Specific Heat Capacity, J/kg-K 470
500
Thermal Conductivity, W/m-K 43
14
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.8
19
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 1.6
3.7
Embodied Energy, MJ/kg 21
53
Embodied Water, L/kg 52
170

Common Calculations

PREN (Pitting Resistance) 2.8
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
220
Resilience: Unit (Modulus of Resilience), kJ/m3 260
260
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19
25
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 12
3.7
Thermal Shock Resistance, points 16
16

Alloy Composition

Aluminum (Al), % 0
0.8 to 1.5
Carbon (C), % 0.1 to 0.2
0.16 to 0.24
Chromium (Cr), % 0.8 to 1.3
17 to 19.5
Iron (Fe), % 96.4 to 98.3
56.7 to 65.3
Manganese (Mn), % 0.3 to 0.8
0 to 2.0
Molybdenum (Mo), % 0.44 to 0.65
0
Nickel (Ni), % 0
13.5 to 16
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0.1 to 0.6
3.2 to 4.0
Sulfur (S), % 0 to 0.040
0 to 0.030