ASTM A182 Grade F24 vs. 70Ag-30Ni Alloy

ASTM A182 grade F24 belongs to the iron alloys classification, while 70Ag-30Ni alloy belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (16, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is 70Ag-30Ni alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
100
Poisson's Ratio 0.29
0.35
Shear Modulus, GPa 74
39
Tensile Strength: Ultimate (UTS), MPa 670
320 to 530

Thermal Properties

Latent Heat of Fusion, J/g 260
170
Melting Completion (Liquidus), °C 1470
960
Melting Onset (Solidus), °C 1430
960
Specific Heat Capacity, J/kg-K 470
300
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
69
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
62

Otherwise Unclassified Properties

Density, g/cm3 7.8
10

Common Calculations

Stiffness to Weight: Axial, points 13
5.8
Stiffness to Weight: Bending, points 24
16
Strength to Weight: Axial, points 24
8.8 to 15
Strength to Weight: Bending, points 22
10 to 15
Thermal Shock Resistance, points 19
13 to 21

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0
Chromium (Cr), % 2.2 to 2.6
0
Iron (Fe), % 94.5 to 96.1
0
Manganese (Mn), % 0.3 to 0.7
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
28.8 to 31
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0.15 to 0.45
0
Silver (Ag), % 0
69 to 71
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0
Residuals, % 0
0 to 0.2