ASTM A182 Grade F24 vs. ASTM A210 Steel

Both ASTM A182 grade F24 and ASTM A210 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is ASTM A210 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
140 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
34
Fatigue Strength, MPa 330
230 to 250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
320 to 360
Tensile Strength: Ultimate (UTS), MPa 670
470 to 540
Tensile Strength: Yield (Proof), MPa 460
290 to 310

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460 to 1470
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
52 to 53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.0 to 8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
18
Embodied Water, L/kg 61
45 to 46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 570
230 to 250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
17 to 19
Strength to Weight: Bending, points 22
17 to 19
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 19
15 to 17