ASTM A182 Grade F24 vs. ASTM A283 Carbon Steel

Both ASTM A182 grade F24 and ASTM A283 carbon steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is ASTM A283 carbon steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
110 to 140
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
26 to 34
Fatigue Strength, MPa 330
150 to 190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
240 to 310
Tensile Strength: Ultimate (UTS), MPa 670
360 to 480
Tensile Strength: Yield (Proof), MPa 460
180 to 260

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
51 to 53
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
1.8
Density, g/cm3 7.8
7.8 to 7.9
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
18
Embodied Water, L/kg 61
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
100 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 570
91 to 180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
13 to 17
Strength to Weight: Bending, points 22
14 to 17
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 19
11 to 15