ASTM A182 Grade F24 vs. Commercially Pure Zirconium

ASTM A182 grade F24 belongs to the iron alloys classification, while commercially pure zirconium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is commercially pure zirconium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
98
Elongation at Break, % 23
18
Fatigue Strength, MPa 330
60
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 74
36
Tensile Strength: Ultimate (UTS), MPa 670
430
Tensile Strength: Yield (Proof), MPa 460
240

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Specific Heat Capacity, J/kg-K 470
270
Thermal Conductivity, W/m-K 39
22
Thermal Expansion, µm/m-K 13
5.5

Otherwise Unclassified Properties

Density, g/cm3 7.8
6.7
Embodied Water, L/kg 61
450

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
65
Resilience: Unit (Modulus of Resilience), kJ/m3 570
290
Stiffness to Weight: Axial, points 13
8.1
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 24
18
Strength to Weight: Bending, points 22
19
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 19
56

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.050
Chromium (Cr), % 2.2 to 2.6
0 to 0.2
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 94.5 to 96.1
0 to 0.2
Manganese (Mn), % 0.3 to 0.7
0
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.12
0 to 0.025
Oxygen (O), % 0
0 to 0.16
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0.15 to 0.45
0
Sulfur (S), % 0 to 0.010
0
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0
Zirconium (Zr), % 0
94.7 to 100