ASTM A182 Grade F24 vs. EN 1.0255 Steel

Both ASTM A182 grade F24 and EN 1.0255 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.0255 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
120
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
27
Fatigue Strength, MPa 330
180
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
280
Tensile Strength: Ultimate (UTS), MPa 670
430
Tensile Strength: Yield (Proof), MPa 460
250

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
40
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.5
Embodied Energy, MJ/kg 33
19
Embodied Water, L/kg 61
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
100
Resilience: Unit (Modulus of Resilience), kJ/m3 570
160
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
15
Strength to Weight: Bending, points 22
16
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 19
14

Alloy Composition

Aluminum (Al), % 0 to 0.020
0.020 to 0.2
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.16
Chromium (Cr), % 2.2 to 2.6
0 to 0.3
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 94.5 to 96.1
94.1 to 99.98
Manganese (Mn), % 0.3 to 0.7
0 to 1.2
Molybdenum (Mo), % 0.9 to 1.1
0 to 0.080
Nickel (Ni), % 0
0 to 0.3
Niobium (Nb), % 0
0 to 0.010
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.45
0 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0 to 0.040
Vanadium (V), % 0.2 to 0.3
0 to 0.020