ASTM A182 Grade F24 vs. EN 1.0511 Steel

Both ASTM A182 grade F24 and EN 1.0511 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.0511 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
17
Fatigue Strength, MPa 330
200
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
370
Tensile Strength: Ultimate (UTS), MPa 670
590
Tensile Strength: Yield (Proof), MPa 460
300

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
48
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
19
Embodied Water, L/kg 61
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
84
Resilience: Unit (Modulus of Resilience), kJ/m3 570
230
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
21
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.37 to 0.44
Chromium (Cr), % 2.2 to 2.6
0 to 0.4
Iron (Fe), % 94.5 to 96.1
97.4 to 99.13
Manganese (Mn), % 0.3 to 0.7
0.5 to 0.8
Molybdenum (Mo), % 0.9 to 1.1
0 to 0.1
Nickel (Ni), % 0
0 to 0.4
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0.15 to 0.45
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.045
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0