MakeItFrom.com
Menu (ESC)

ASTM A182 Grade F24 vs. EN 1.4057 Stainless Steel

Both ASTM A182 grade F24 and EN 1.4057 stainless steel are iron alloys. They have 84% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.4057 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
11 to 17
Fatigue Strength, MPa 330
320 to 430
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 420
520 to 580
Tensile Strength: Ultimate (UTS), MPa 670
840 to 980
Tensile Strength: Yield (Proof), MPa 460
530 to 790

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 460
850
Melting Completion (Liquidus), °C 1470
1440
Melting Onset (Solidus), °C 1430
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
9.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.3
2.2
Embodied Energy, MJ/kg 33
32
Embodied Water, L/kg 61
120

Common Calculations

PREN (Pitting Resistance) 6.7
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
96 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 570
700 to 1610
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
30 to 35
Strength to Weight: Bending, points 22
26 to 28
Thermal Diffusivity, mm2/s 11
6.7
Thermal Shock Resistance, points 19
30 to 35

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.12 to 0.22
Chromium (Cr), % 2.2 to 2.6
15 to 17
Iron (Fe), % 94.5 to 96.1
77.7 to 83.4
Manganese (Mn), % 0.3 to 0.7
0 to 1.5
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
1.5 to 2.5
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0.15 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0