ASTM A182 Grade F24 vs. EN 1.4162 Stainless Steel

Both ASTM A182 grade F24 and EN 1.4162 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.4162 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
250
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
32
Fatigue Strength, MPa 330
410
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
78
Shear Strength, MPa 420
520
Tensile Strength: Ultimate (UTS), MPa 670
780
Tensile Strength: Yield (Proof), MPa 460
520

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 460
1000
Melting Completion (Liquidus), °C 1470
1420
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.3
2.6
Embodied Energy, MJ/kg 33
38
Embodied Water, L/kg 61
150

Common Calculations

PREN (Pitting Resistance) 6.7
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
220
Resilience: Unit (Modulus of Resilience), kJ/m3 570
690
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
28
Strength to Weight: Bending, points 22
25
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 19
21

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.040
Chromium (Cr), % 2.2 to 2.6
21 to 22
Copper (Cu), % 0
0.1 to 0.8
Iron (Fe), % 94.5 to 96.1
67.2 to 73.3
Manganese (Mn), % 0.3 to 0.7
4.0 to 6.0
Molybdenum (Mo), % 0.9 to 1.1
0.1 to 0.8
Nickel (Ni), % 0
1.4 to 1.9
Nitrogen (N), % 0 to 0.12
0.2 to 0.25
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0.15 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0