ASTM A182 Grade F24 vs. EN 1.4313 Stainless Steel

Both ASTM A182 grade F24 and EN 1.4313 stainless steel are iron alloys. They have 85% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.4313 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
12 to 17
Fatigue Strength, MPa 330
340 to 510
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Shear Strength, MPa 420
460 to 600
Tensile Strength: Ultimate (UTS), MPa 670
750 to 1000
Tensile Strength: Yield (Proof), MPa 460
580 to 910

Thermal Properties

Latent Heat of Fusion, J/g 260
280
Maximum Temperature: Mechanical, °C 460
780
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
10
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
2.4
Embodied Energy, MJ/kg 33
34
Embodied Water, L/kg 61
110

Common Calculations

PREN (Pitting Resistance) 6.7
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110 to 150
Resilience: Unit (Modulus of Resilience), kJ/m3 570
870 to 2100
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
27 to 36
Strength to Weight: Bending, points 22
23 to 28
Thermal Diffusivity, mm2/s 11
6.7
Thermal Shock Resistance, points 19
27 to 36

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.050
Chromium (Cr), % 2.2 to 2.6
12 to 14
Iron (Fe), % 94.5 to 96.1
78.5 to 84.2
Manganese (Mn), % 0.3 to 0.7
0 to 1.5
Molybdenum (Mo), % 0.9 to 1.1
0.3 to 0.7
Nickel (Ni), % 0
3.5 to 4.5
Nitrogen (N), % 0 to 0.12
0 to 0.020
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0.15 to 0.45
0 to 0.7
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0