ASTM A182 Grade F24 vs. EN 1.4376 Stainless Steel

Both ASTM A182 grade F24 and EN 1.4376 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.4376 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
230
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
45
Fatigue Strength, MPa 330
420
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 420
530
Tensile Strength: Ultimate (UTS), MPa 670
750
Tensile Strength: Yield (Proof), MPa 460
450

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 460
930
Melting Completion (Liquidus), °C 1470
1410
Melting Onset (Solidus), °C 1430
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.3
2.6
Embodied Energy, MJ/kg 33
37
Embodied Water, L/kg 61
140

Common Calculations

PREN (Pitting Resistance) 6.7
21
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
290
Resilience: Unit (Modulus of Resilience), kJ/m3 570
520
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
27
Strength to Weight: Bending, points 22
24
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 19
17

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.1
Chromium (Cr), % 2.2 to 2.6
17 to 20.5
Iron (Fe), % 94.5 to 96.1
65.5 to 76
Manganese (Mn), % 0.3 to 0.7
5.0 to 8.0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
2.0 to 4.5
Nitrogen (N), % 0 to 0.12
0 to 0.3
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0.15 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0