ASTM A182 Grade F24 vs. EN 1.4835 Stainless Steel

Both ASTM A182 grade F24 and EN 1.4835 stainless steel are iron alloys. They have 69% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.4835 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
180
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
43
Fatigue Strength, MPa 330
310
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
77
Shear Strength, MPa 420
520
Tensile Strength: Ultimate (UTS), MPa 670
750
Tensile Strength: Yield (Proof), MPa 460
350

Thermal Properties

Latent Heat of Fusion, J/g 260
320
Maximum Temperature: Mechanical, °C 460
1150
Melting Completion (Liquidus), °C 1470
1400
Melting Onset (Solidus), °C 1430
1360
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.0
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
17
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 2.3
3.3
Embodied Energy, MJ/kg 33
47
Embodied Water, L/kg 61
160

Common Calculations

PREN (Pitting Resistance) 6.7
24
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
270
Resilience: Unit (Modulus of Resilience), kJ/m3 570
310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
27
Strength to Weight: Bending, points 22
24
Thermal Diffusivity, mm2/s 11
4.0
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.050 to 0.12
Cerium (Ce), % 0
0.030 to 0.080
Chromium (Cr), % 2.2 to 2.6
20 to 22
Iron (Fe), % 94.5 to 96.1
62 to 68.4
Manganese (Mn), % 0.3 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
10 to 12
Nitrogen (N), % 0 to 0.12
0.12 to 0.2
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0.15 to 0.45
1.4 to 2.5
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0