ASTM A182 Grade F24 vs. EN 1.4913 Stainless Steel

Both ASTM A182 grade F24 and EN 1.4913 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.4913 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
14 to 22
Fatigue Strength, MPa 330
320 to 480
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
75
Shear Strength, MPa 420
550 to 590
Tensile Strength: Ultimate (UTS), MPa 670
870 to 980
Tensile Strength: Yield (Proof), MPa 460
480 to 850

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 460
700
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
24
Thermal Expansion, µm/m-K 13
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
9.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
2.9
Embodied Energy, MJ/kg 33
41
Embodied Water, L/kg 61
97

Common Calculations

PREN (Pitting Resistance) 6.7
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
130 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 570
600 to 1860
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
31 to 35
Strength to Weight: Bending, points 22
26 to 28
Thermal Diffusivity, mm2/s 11
6.5
Thermal Shock Resistance, points 19
31 to 34

Alloy Composition

Aluminum (Al), % 0 to 0.020
0 to 0.020
Boron (B), % 0.0015 to 0.0070
0 to 0.0015
Carbon (C), % 0.050 to 0.1
0.17 to 0.23
Chromium (Cr), % 2.2 to 2.6
10 to 11.5
Iron (Fe), % 94.5 to 96.1
84.5 to 88.3
Manganese (Mn), % 0.3 to 0.7
0.4 to 0.9
Molybdenum (Mo), % 0.9 to 1.1
0.5 to 0.8
Nickel (Ni), % 0
0.2 to 0.6
Niobium (Nb), % 0
0.25 to 0.55
Nitrogen (N), % 0 to 0.12
0.050 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.45
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0.1 to 0.3