ASTM A182 Grade F24 vs. EN 1.5450 Steel

Both ASTM A182 grade F24 and EN 1.5450 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.5450 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
19
Fatigue Strength, MPa 330
310
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
380
Tensile Strength: Ultimate (UTS), MPa 670
620
Tensile Strength: Yield (Proof), MPa 460
460

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
410
Melting Completion (Liquidus), °C 1470
1470
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
49
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
2.4
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.5
Embodied Energy, MJ/kg 33
20
Embodied Water, L/kg 61
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110
Resilience: Unit (Modulus of Resilience), kJ/m3 570
550
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
22
Strength to Weight: Bending, points 22
20
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 19
18

Alloy Composition

Aluminum (Al), % 0 to 0.020
0 to 0.060
Boron (B), % 0.0015 to 0.0070
0.0020 to 0.0060
Carbon (C), % 0.050 to 0.1
0.060 to 0.1
Chromium (Cr), % 2.2 to 2.6
0 to 0.2
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 94.5 to 96.1
97.6 to 98.8
Manganese (Mn), % 0.3 to 0.7
0.6 to 0.8
Molybdenum (Mo), % 0.9 to 1.1
0.4 to 0.5
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.45
0.1 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0.060 to 0.1
0 to 0.060
Vanadium (V), % 0.2 to 0.3
0