ASTM A182 Grade F24 vs. EN 1.6582 Steel

Both ASTM A182 grade F24 and EN 1.6582 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.6582 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
190 to 300
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Tensile Strength: Ultimate (UTS), MPa 670
620 to 1750

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
440
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
40
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
3.6
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.7
Embodied Energy, MJ/kg 33
22
Embodied Water, L/kg 61
56

Common Calculations

PREN (Pitting Resistance) 6.7
2.2
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
22 to 62
Strength to Weight: Bending, points 22
21 to 41
Thermal Diffusivity, mm2/s 11
11
Thermal Shock Resistance, points 19
18 to 51

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.3 to 0.38
Chromium (Cr), % 2.2 to 2.6
1.3 to 1.7
Iron (Fe), % 94.5 to 96.1
94.7 to 96.5
Manganese (Mn), % 0.3 to 0.7
0.5 to 0.8
Molybdenum (Mo), % 0.9 to 1.1
0.15 to 0.3
Nickel (Ni), % 0
1.3 to 1.7
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0.15 to 0.45
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.035
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0