ASTM A182 Grade F24 vs. EN 1.7367 Steel

Both ASTM A182 grade F24 and EN 1.7367 steel are iron alloys. Both are furnished in the normalized and tempered condition. They have a moderately high 93% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.7367 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
18
Fatigue Strength, MPa 330
310
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
75
Tensile Strength: Ultimate (UTS), MPa 670
670
Tensile Strength: Yield (Proof), MPa 460
460

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 460
600
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
26
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
8.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
10

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
2.6
Embodied Energy, MJ/kg 33
37
Embodied Water, L/kg 61
88

Common Calculations

PREN (Pitting Resistance) 6.7
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
110
Resilience: Unit (Modulus of Resilience), kJ/m3 570
560
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
24
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 11
6.9
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0 to 0.020
0 to 0.020
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.080 to 0.12
Chromium (Cr), % 2.2 to 2.6
8.0 to 9.5
Iron (Fe), % 94.5 to 96.1
87.3 to 90.3
Manganese (Mn), % 0.3 to 0.7
0.3 to 0.6
Molybdenum (Mo), % 0.9 to 1.1
0.85 to 1.1
Nickel (Ni), % 0
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0 to 0.12
0.030 to 0.070
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0.15 to 0.45
0.2 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0.060 to 0.1
0 to 0.010
Vanadium (V), % 0.2 to 0.3
0.18 to 0.25
Zirconium (Zr), % 0
0 to 0.010