ASTM A182 Grade F24 vs. EN 1.8874 Steel

Both ASTM A182 grade F24 and EN 1.8874 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is EN 1.8874 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
19
Fatigue Strength, MPa 330
340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
410
Tensile Strength: Ultimate (UTS), MPa 670
660
Tensile Strength: Yield (Proof), MPa 460
500

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
420
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
39
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.9

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
3.2
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.8
Embodied Energy, MJ/kg 33
24
Embodied Water, L/kg 61
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
120
Resilience: Unit (Modulus of Resilience), kJ/m3 570
670
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
23
Strength to Weight: Bending, points 22
21
Thermal Diffusivity, mm2/s 11
10
Thermal Shock Resistance, points 19
19

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0 to 0.0050
Carbon (C), % 0.050 to 0.1
0 to 0.18
Chromium (Cr), % 2.2 to 2.6
0 to 1.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 94.5 to 96.1
93.6 to 100
Manganese (Mn), % 0.3 to 0.7
0 to 1.7
Molybdenum (Mo), % 0.9 to 1.1
0 to 0.7
Nickel (Ni), % 0
0 to 1.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0 to 0.12
0 to 0.015
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.45
0 to 0.6
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0.060 to 0.1
0 to 0.050
Vanadium (V), % 0.2 to 0.3
0 to 0.080
Zirconium (Zr), % 0
0 to 0.15