ASTM A182 Grade F24 vs. SAE-AISI 12L14 Steel

Both ASTM A182 grade F24 and SAE-AISI 12L14 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is SAE-AISI 12L14 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
140 to 170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
11 to 25
Fatigue Strength, MPa 330
190 to 290
Poisson's Ratio 0.29
0.29
Reduction in Area, % 45
39 to 51
Shear Modulus, GPa 74
72
Shear Strength, MPa 420
280 to 370
Tensile Strength: Ultimate (UTS), MPa 670
440 to 620
Tensile Strength: Yield (Proof), MPa 460
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
1.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
18
Embodied Water, L/kg 61
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
64 to 93
Resilience: Unit (Modulus of Resilience), kJ/m3 570
180 to 560
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
15 to 22
Strength to Weight: Bending, points 22
16 to 20
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 19
14 to 20

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.15
Chromium (Cr), % 2.2 to 2.6
0
Iron (Fe), % 94.5 to 96.1
97.9 to 98.7
Lead (Pb), % 0
0.15 to 0.35
Manganese (Mn), % 0.3 to 0.7
0.85 to 1.2
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0.040 to 0.090
Silicon (Si), % 0.15 to 0.45
0
Sulfur (S), % 0 to 0.010
0.26 to 0.35
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0