ASTM A182 Grade F24 vs. SAE-AISI 1330 Steel

Both ASTM A182 grade F24 and SAE-AISI 1330 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is SAE-AISI 1330 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
150 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
11 to 23
Fatigue Strength, MPa 330
210 to 380
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
73
Shear Strength, MPa 420
330 to 430
Tensile Strength: Ultimate (UTS), MPa 670
520 to 710
Tensile Strength: Yield (Proof), MPa 460
290 to 610

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
400
Melting Completion (Liquidus), °C 1470
1460
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.4
Embodied Energy, MJ/kg 33
19
Embodied Water, L/kg 61
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
76 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 570
230 to 990
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
19 to 25
Strength to Weight: Bending, points 22
18 to 23
Thermal Diffusivity, mm2/s 11
14
Thermal Shock Resistance, points 19
17 to 23

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.28 to 0.33
Chromium (Cr), % 2.2 to 2.6
0
Iron (Fe), % 94.5 to 96.1
97.3 to 98
Manganese (Mn), % 0.3 to 0.7
1.6 to 1.9
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.035
Silicon (Si), % 0.15 to 0.45
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.040
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0