ASTM A182 Grade F24 vs. SAE-AISI 52100 Steel

Both ASTM A182 grade F24 and SAE-AISI 52100 steel are iron alloys. They have a very high 97% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is SAE-AISI 52100 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
180 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
10 to 20
Fatigue Strength, MPa 330
250 to 340
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Shear Strength, MPa 420
370 to 420
Tensile Strength: Ultimate (UTS), MPa 670
590 to 2010
Tensile Strength: Yield (Proof), MPa 460
360 to 560

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 460
430
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 39
47
Thermal Expansion, µm/m-K 13
12 to 13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
1.5
Embodied Energy, MJ/kg 33
20
Embodied Water, L/kg 61
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
54 to 310
Resilience: Unit (Modulus of Resilience), kJ/m3 570
350 to 840
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
21 to 72
Strength to Weight: Bending, points 22
20 to 45
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 19
19 to 61

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0.93 to 1.1
Chromium (Cr), % 2.2 to 2.6
1.4 to 1.6
Iron (Fe), % 94.5 to 96.1
96.5 to 97.3
Manganese (Mn), % 0.3 to 0.7
0.25 to 0.45
Molybdenum (Mo), % 0.9 to 1.1
0
Nitrogen (N), % 0 to 0.12
0
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0.15 to 0.45
0.15 to 0.35
Sulfur (S), % 0 to 0.010
0 to 0.015
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0