ASTM A182 Grade F24 vs. S28200 Stainless Steel

Both ASTM A182 grade F24 and S28200 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is S28200 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
45
Fatigue Strength, MPa 330
430
Poisson's Ratio 0.29
0.28
Reduction in Area, % 45
57
Shear Modulus, GPa 74
77
Shear Strength, MPa 420
610
Tensile Strength: Ultimate (UTS), MPa 670
870
Tensile Strength: Yield (Proof), MPa 460
460

Thermal Properties

Latent Heat of Fusion, J/g 260
290
Maximum Temperature: Mechanical, °C 460
900
Melting Completion (Liquidus), °C 1470
1380
Melting Onset (Solidus), °C 1430
1330
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
18

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
12
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 2.3
2.8
Embodied Energy, MJ/kg 33
41
Embodied Water, L/kg 61
160

Common Calculations

PREN (Pitting Resistance) 6.7
29
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
330
Resilience: Unit (Modulus of Resilience), kJ/m3 570
540
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 24
32
Strength to Weight: Bending, points 22
27
Thermal Shock Resistance, points 19
17

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.15
Chromium (Cr), % 2.2 to 2.6
17 to 19
Copper (Cu), % 0
0.75 to 1.3
Iron (Fe), % 94.5 to 96.1
57.7 to 64.1
Manganese (Mn), % 0.3 to 0.7
17 to 19
Molybdenum (Mo), % 0.9 to 1.1
0.75 to 1.3
Nitrogen (N), % 0 to 0.12
0.4 to 0.6
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0.15 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0.060 to 0.1
0
Vanadium (V), % 0.2 to 0.3
0