ASTM A182 Grade F24 vs. S40910 Stainless Steel

Both ASTM A182 grade F24 and S40910 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F24 and the bottom bar is S40910 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
23
Fatigue Strength, MPa 330
130
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
75
Shear Strength, MPa 420
270
Tensile Strength: Ultimate (UTS), MPa 670
430
Tensile Strength: Yield (Proof), MPa 460
190

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 460
710
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
26
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 4.0
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.3
2.0
Embodied Energy, MJ/kg 33
28
Embodied Water, L/kg 61
94

Common Calculations

PREN (Pitting Resistance) 6.7
11
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
80
Resilience: Unit (Modulus of Resilience), kJ/m3 570
94
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
16
Strength to Weight: Bending, points 22
16
Thermal Diffusivity, mm2/s 11
6.9
Thermal Shock Resistance, points 19
16

Alloy Composition

Aluminum (Al), % 0 to 0.020
0
Boron (B), % 0.0015 to 0.0070
0
Carbon (C), % 0.050 to 0.1
0 to 0.030
Chromium (Cr), % 2.2 to 2.6
10.5 to 11.7
Iron (Fe), % 94.5 to 96.1
85 to 89.5
Manganese (Mn), % 0.3 to 0.7
0 to 1.0
Molybdenum (Mo), % 0.9 to 1.1
0
Nickel (Ni), % 0
0 to 0.5
Niobium (Nb), % 0
0 to 0.17
Nitrogen (N), % 0 to 0.12
0 to 0.030
Phosphorus (P), % 0 to 0.020
0 to 0.040
Silicon (Si), % 0.15 to 0.45
0 to 1.0
Sulfur (S), % 0 to 0.010
0 to 0.020
Titanium (Ti), % 0.060 to 0.1
0 to 0.5
Vanadium (V), % 0.2 to 0.3
0