ASTM A182 Grade F3V vs. S32205 Stainless Steel

Both ASTM A182 grade F3V and S32205 stainless steel are iron alloys. Both are furnished in the annealed condition. They have 72% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A182 grade F3V and the bottom bar is S32205 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 210
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 20
28
Fatigue Strength, MPa 330
370
Poisson's Ratio 0.29
0.27
Reduction in Area, % 51
51
Shear Modulus, GPa 74
80
Shear Strength, MPa 410
480
Tensile Strength: Ultimate (UTS), MPa 660
740
Tensile Strength: Yield (Proof), MPa 470
510

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 470
1070
Melting Completion (Liquidus), °C 1470
1450
Melting Onset (Solidus), °C 1430
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 39
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.6
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.8
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 4.2
18
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.3
3.7
Embodied Energy, MJ/kg 33
50
Embodied Water, L/kg 63
160

Common Calculations

PREN (Pitting Resistance) 6.3
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
190
Resilience: Unit (Modulus of Resilience), kJ/m3 590
630
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23
26
Strength to Weight: Bending, points 21
23
Thermal Diffusivity, mm2/s 10
4.0
Thermal Shock Resistance, points 19
20

Alloy Composition

Boron (B), % 0.0010 to 0.0030
0
Carbon (C), % 0.050 to 0.18
0 to 0.030
Chromium (Cr), % 2.8 to 3.2
22 to 23
Iron (Fe), % 94.4 to 95.7
63.7 to 70.4
Manganese (Mn), % 0.3 to 0.6
0 to 2.0
Molybdenum (Mo), % 0.9 to 1.1
3.0 to 3.5
Nickel (Ni), % 0
4.5 to 6.5
Nitrogen (N), % 0
0.14 to 0.2
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.1
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.020
Titanium (Ti), % 0.015 to 0.035
0
Vanadium (V), % 0.2 to 0.3
0