ASTM A202 Steel vs. ASTM A387 Grade 21L Class 1

Both ASTM A202 steel and ASTM A387 grade 21L class 1 are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is ASTM A387 grade 21L class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 200
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 18
21
Fatigue Strength, MPa 240
160
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 360 to 410
310
Tensile Strength: Ultimate (UTS), MPa 590 to 670
500
Tensile Strength: Yield (Proof), MPa 350 to 360
230

Thermal Properties

Latent Heat of Fusion, J/g 260
260
Maximum Temperature: Mechanical, °C 410
480
Melting Completion (Liquidus), °C 1450
1470
Melting Onset (Solidus), °C 1410
1430
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
41
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.6
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.8

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
4.1
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.8
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 49
62

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 96
84
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 350
140
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 24
18
Strength to Weight: Bending, points 20 to 22
18
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 17 to 20
14