ASTM A202 Steel vs. EN 1.3532 Steel

Both ASTM A202 steel and EN 1.3532 steel are iron alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is EN 1.3532 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 200
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 590 to 670
700 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 260
250
Maximum Temperature: Mechanical, °C 410
440
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
9.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
5.0
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.9
Embodied Energy, MJ/kg 19
25
Embodied Water, L/kg 49
60

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 21 to 24
25 to 50
Strength to Weight: Bending, points 20 to 22
22 to 36
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 17 to 20
21 to 42

Comparable Variants