ASTM A202 Steel vs. EN 1.3961 Alloy

Both ASTM A202 steel and EN 1.3961 alloy are iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is EN 1.3961 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 17 to 18
31
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 73
72
Shear Strength, MPa 360 to 410
300
Tensile Strength: Ultimate (UTS), MPa 590 to 670
450
Tensile Strength: Yield (Proof), MPa 350 to 360
310

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Melting Completion (Liquidus), °C 1450
1430
Melting Onset (Solidus), °C 1410
1390
Specific Heat Capacity, J/kg-K 470
460
Thermal Expansion, µm/m-K 13
1.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
25
Density, g/cm3 7.8
8.2
Embodied Carbon, kg CO2/kg material 1.4
4.8
Embodied Energy, MJ/kg 19
66
Embodied Water, L/kg 49
110

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 96
130
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 350
250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 21 to 24
15
Strength to Weight: Bending, points 20 to 22
16
Thermal Shock Resistance, points 17 to 20
130