ASTM A202 Steel vs. Monel R-405

ASTM A202 steel belongs to the iron alloys classification, while Monel R-405 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is ASTM A202 steel and the bottom bar is Monel R-405.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
160
Elongation at Break, % 17 to 18
9.1 to 39
Fatigue Strength, MPa 240
210 to 250
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 73
62
Shear Strength, MPa 360 to 410
350 to 370
Tensile Strength: Ultimate (UTS), MPa 590 to 670
540 to 630
Tensile Strength: Yield (Proof), MPa 350 to 360
190 to 350

Thermal Properties

Latent Heat of Fusion, J/g 260
270
Maximum Temperature: Mechanical, °C 410
900
Melting Completion (Liquidus), °C 1450
1350
Melting Onset (Solidus), °C 1410
1300
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 52
23
Thermal Expansion, µm/m-K 13
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
50
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.4
7.9
Embodied Energy, MJ/kg 19
110
Embodied Water, L/kg 49
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93 to 96
49 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 330 to 350
120 to 370
Stiffness to Weight: Axial, points 13
10
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 21 to 24
17 to 20
Strength to Weight: Bending, points 20 to 22
17 to 18
Thermal Diffusivity, mm2/s 14
5.9
Thermal Shock Resistance, points 17 to 20
17 to 20

Comparable Variants