ASTM A202 Steel vs. C35300 Brass
ASTM A202 steel belongs to the iron alloys classification, while C35300 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is ASTM A202 steel and the bottom bar is C35300 brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 100 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 73 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 590 to 670 | |
| 340 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 410 | |
| 120 |
| Melting Completion (Liquidus), °C | 1450 | |
| 910 |
| Melting Onset (Solidus), °C | 1410 | |
| 890 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 52 | |
| 120 |
| Thermal Expansion, µm/m-K | 13 | |
| 21 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 26 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 29 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 23 |
| Density, g/cm3 | 7.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.6 |
| Embodied Energy, MJ/kg | 19 | |
| 45 |
| Embodied Water, L/kg | 49 | |
| 320 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 21 to 24 | |
| 12 to 22 |
| Strength to Weight: Bending, points | 20 to 22 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 14 | |
| 38 |
| Thermal Shock Resistance, points | 17 to 20 | |
| 11 to 22 |